Ideal 46-322
IDEAL Thermo-Shrink 46-322 Economy Heat Shrink Tubing, 0.539 in ID Expanded, 0.252 in ID Recovered, 0.026 in THK Wall Recovered, 6 in L, Polyolefin, Black
Heatshrink
6809128
46-322
Ideal
$0.00
/ ea
IDEAL, Heat Shrinkable Tube, Thermo-Shrink, Thin-Wall, Shrink Ratio: 2:1, Outside Diameter: 0.500 IN, Thickness: 026 IN, Length: 6 IN, Dielectric Strength: 20 KV/MM For ASTM D 150 Test Method, Volume Resistivity: 1014 OHM CM For ASTM D 876 Test Method, Continuous Operating Temperature: -55 To 125 DEG C, Minimum Shrink Temperature: 70 DEG C, Heat Shock: No cracking For UL 224(250 DEG C /4 hours), Cable Range: 4 - 1 AWG, Nominal Recoveredi.d. (max.): 0.252 IN, Expanded I.d. (min.): 0.539, Elongation At Break: 600 PCT For ASTM D 638 Test Method, Elongation Of Break After Aging: 350 PCT For UL 224 Test Method, Cold Bend Test (-55°c/4 Hours): No Cracking For UL 224 Test Method, Copper Corrosion: Pass For UL 224 Test Method, Chemical Resistance: Pass For UL 224 Test Method, Longitudinal Shrinkage: 0 Plus Or Minus 5 PCT For UL 224 Test Method, Eccentricity: 30 PCT For UL 224 Test Method, Normal Size: 1/2 IN, Package: Bag
- Features
- Polyolefin material electrically insulates and protects inline components, disconnect terminals and splices with its high strength and excellent resilience
- Use to bundle wires for very flexible light duty harnesses
- It has highly flame-retardant property to resist electric shock and is flexible for convenient operation
- Resistant to common fluids and solvents
- 14 Mpa tensile strength and 20 kV/mil dielectric strength
- It can be elongated up to 350% of the original size after aging at 175 deg C for about 168 hr
- 30% eccentricity
- +/-5% longitudinal shrinkage
- -55 deg C/4 hr cold blend test no cracking for UL 224 test method
- Copper corrosion and chemical resistance pass for UL 224 test method
- 600% elongation at break for ASTM D638 test method
- 350% elongation of break after aging for UL 224 test method
- 1/2 in normal
- No PBBs and PBBEs